ZCR01 PCR聚烯烴熱縮短膜
這(zhe)是一種大批利用PCR回(hui)料(liao)（Post Customer Recycled material 花費(fei)后再收(shou)受接管料(liao)）而出產的聚烯烴(jing)熱縮短膜，膜中(zhong)PCR料(liao)占比30%，該膜已經由過程了GRS4.0認(ren)(ren)證(zheng)（環球收(shou)受接管規范認(ren)(ren)證(zheng)）。
該膜(mo)除(chu)利(li)用大批PCR回料(liao)外，其出產工藝與ZDF01根(gen)(gen)基(ji)不異，產物特征及利(li)用范(fan)疇，與ZDF01膜(mo)也根(gen)(gen)基(ji)不異，一樣(yang)具(ju)備力學機(ji)能好、熱封性好，縮短率高檔(dang)長處，對各類包裝機(ji)的(de)順應(ying)性也很好。
產物利用
機能參數
| TEST ITEM | UNIT | ASTM TEST | TYPICAL VALUES | |||||||||
| INTRODUCTION | ||||||||||||
| Post Consumer Recycling | 30%Recycled post-consumer polyethylene(RM0193) | |||||||||||
| Gauge 厚度 | 15um | 19um | 25um | 30um | ||||||||
| TENSILE | ||||||||||||
| Tensile Strength (MD) 拉伸強度 | N/mm2 | D882 | 115 | 110 | 90 | 88 | ||||||
| Tensile Strength (TD) | 110 | 105 | 85 | 80 | ||||||||
| Elongation(MD) 斷裂伸長率 | % | 105 | 110 | 105 | 100 | |||||||
| Elongation (TD) | 100 | 105 | 95 | 90 | ||||||||
| TEAR 扯破強度 | ||||||||||||
| MD at 400gm | gf | D1922 | 10.5 | 13.5 | 16.5 | 20.5 | ||||||
| TD at 400gm | 9.8 | 12.5 | 16.5 | 22.5 | ||||||||
| SEAL STRENGTH 熱封強度 | ||||||||||||
| MD\Hot Wire Seal | N/mm | F88 | 0.85 | 0.95 | 1.15 | 1.35 | ||||||
| TD\Hot Wire Seal | 1.05 | 1.15 | 1.25 | 1.55 | ||||||||
| COF (Film To Film) | - | |||||||||||
| Static 靜磨擦 | D1894 | 0.20 | 0.18 | 0.22 | 0.23 | |||||||
| Dynamic 動磨擦 | 0.20 | 0.18 | 0.22 | 0.23 | ||||||||
| OPTICS | ||||||||||||
| Haze 霧度 | D1003 | 3.5 | 3.8 | 4.0 | 4.3 | |||||||
| Clarity 通明度 | D1746 | 93.0 | 92.0 | 91.0 | 90.0 | |||||||
| Gloss @ 45Deg 光芒度 | D2457 | 85.0 | 82.0 | 80.0 | 81.0 | |||||||
| BARRIER 隔絕性 | ||||||||||||
| Oxygen Transmission Rate 透氧率 | cc/㎡/day | D3985 | 9200 | 8200 | 5600 | 4200 | ||||||
| Water Vapor Transmission Rate 透水氣率 | gm/㎡/day | F1249 | 25.9 | 17.2 | 14.5 | 11.2 | ||||||
| SHRINKAGEPROPERTIES 縮短性 | MD | TD | MD | TD | ||||||||
| Free Shrinkage 縮短率 | 100℃ | % | D2732 | 17 | 26 | 14 | 23 | |||||
| 110℃ | 32 | 44 | 29 | 42 | ||||||||
| 120℃ | 54 | 59 | 53 | 60 | ||||||||
| 130℃ | 68 | 69 | 68 | 69 | ||||||||
| MD | MD | TD | TD | |||||||||
| Shrink Tension 縮短張力 | 100℃ | Mpa | D2838 | 1.65 | 2.35 | 1.70 | 2.25 | |||||
| 110℃ | 2.55 | 3.20 | 2.65 | 3.45 | ||||||||
| 120℃ | 2.70 | 3.45 | 2.95 | 3.65 | ||||||||
| 130℃ | 2.45 | 3.10 | 2.75 | 3.20 | ||||||||
Note:This information represents our best judgment on the work done, but the company assumes no liability whatsoever in connection with the use of information or findings contained herein.
以(yi)上(shang)資料(liao)是(shi)本公司外部評測之數據(ju)，僅供參考。